Title:Composite Repair for Concrete Bridges Subjected to Alkali-Silica Reaction
Authors:Yail Jimmy Kim
University:University of Colorado Denver
Publication Date:Mar 2022
Report #:MPC-22-455
Project #:MPC-583
TRID #:01848431
Keywords:alkali silica reactions, composite materials, concrete bridges, failure analysis, fiber reinforced polymers
Type:Research Report – MPC Publications

 

Abstract

This report presents a comparative experimental study on the axial behavior of concrete subjected to alkali-silica reaction (ASR) with and without confinement by carbon-fiber reinforced polymer (CFRP) sheets. A total of 120 cylinders are cast using two types of coarse aggregates to represent variable levels of ASR: rhyolite (reactive) substitutes granite (non-reactive) at a replacement ratio ranging from 0% to 100%. As per a test standard, the cylinders are conditioned in a sodium hydroxide (NaOH) solution. The physical properties of the concrete and the solution are measured over time to examine the reciprocal action between the NaOH and rhyolite, followed by microscopic observations on the progression of ASR through the concrete. Sixty cylinders are confined, and all specimens are monotonically loaded to failure. The load-carrying capacity of the confined cylinders noticeably increases compared with that of the plain concrete, while the degree of improvement is controlled by the ASR-damaged concrete core. The cylinders' average toughness decays with ASR, accompanied by irreversible energy dissipation and degraded CFRP-concrete interaction. The failure characteristics of both plain and confined cylinders are also influenced by ASR, dependent upon the replacement ratio, particularly for the integrity of the core. An analytical model is formulated to understand the implications of ASR, including an assessment of an existing design approach, and is further used for design recommendations.

How to Cite

Kim, Yail Jimmy. Composite Repair for Concrete Bridges Subjected to Alkali-Silica Reaction, MPC-22-455. North Dakota State University - Upper Great Plains Transportation Institute, Fargo: Mountain-Plains Consortium, 2022.

NDSU Dept 2880P.O. Box 6050Fargo, ND 58108-6050
(701)231-7767ndsu.ugpti@ndsu.edu